In today’s market, it is imperative to be knowledgeable and have an edge over the competition. ACI members have it…they are engaged, informed, and stay up to date by taking advantage of benefits that ACI membership provides them.
Read more about membership
Become an ACI Member
Founded in 1904 and headquartered in Farmington Hills, Michigan, USA, the American Concrete Institute is a leading authority and resource worldwide for the development, dissemination, and adoption of its consensus-based standards, technical resources, educational programs, and proven expertise for individuals and organizations involved in concrete design, construction, and materials, who share a commitment to pursuing the best use of concrete.
American Concrete Institute
38800 Country Club Dr.
Farmington Hills, MI
Feedback via Email
Home > Publications > International Concrete Abstracts Portal
The International Concrete Abstracts Portal is an ACI led collaboration with leading technical organizations from within the international concrete industry and offers the most comprehensive collection of published concrete abstracts.
Title: Corrosion Deterioration of Steel in Cracked SHCC
Author(s): Suvash Chandra Paul, Gideon Pieter Adriaan Greeff van Zijl
Appears on pages(s): 557–572
Keywords: chloride, corrosion, cracks, steel yield force, pitting depth, mass loss, SHCC.
Abstract:The presence of cracks is unavoidable in reinforced concrete structures and also a gateway for chloride into concrete, leading to corrosion of steel reinforcing bars. So, crack control, crack width limitation and chloride threshold levels are well-established concepts in durability of reinforced concrete structures. This paper reports on accelerated chloride-induced corrosion in cracked reinforced strain-hardening cement-based composites and reinforced mortar beams, both in loaded and unloaded states. Corrosion rates are monitored and loss of mass and yield force, as well as corrosion pitting depth in steel bars are reported. The chloride content at different depths in specimens is also determined through XRF, and through chemical testing of acid and water soluble chloride content by titration. Finally, different relationships are drawn between crack properties, mass loss, yield force, corroded depth and chloride levels at the steel surface for different cover depths. It is found that the crack spacing and free chloride at the steel surface level are best correlated to the corrosion damage in the specimens.