Title: Healing with Polymer Containing Phosphazene of Concrete Exposed to Freezing and Thawing

Author(s): Harun Tanyildizi

Publication: Materials Journal

Volume: 118

Issue: 1

Appears on pages(s): 13-20

Keywords: freezing and thawing; healing; mechanical properties; phosphazene; polymer; strength properties

DOI: 10.14359/51728147

Date: 1/1/2021

This work aims to decrease the damage in concrete caused by freezing-and-thawing. For this, concrete was healed using the polymer containing phosphazene after the freezing and thawing. The Taguchi method was used to decrease the experimental numbers. The experimental variables were determined as cement dosage, the phosphazene percentage, and curing time. 100 × 100 × 100 mm (3.94 × 3.94 × 3.94 in.) cubes were prepared for experiments. After demolding, the samples were cured in a water tank at 20°C ± 2°C (68°F ± 3.6°F) until the test ages (28, 60, 90, 180, and 365 days) were reached. These samples were then subjected to the freezing-and-thawing cycles. The healing process was conducted to the samples by impregnation with the polymer containing phosphazene after freezing-and-thawing cycles. Lastly, the compressive strength, ultrasonic pulse velocity, and weight change of concretes were determined. Scanning electron microscope, energydispersive X-ray spectroscopy, and X-ray powder diffraction analyses were performed to examine the microstructures of the samples. The results showed that the impregnation of polymer containing phosphazene after the freezing-and-thawing increased the strength and durability of the concrete.