In today’s market, it is imperative to be knowledgeable and have an edge over the competition. ACI members have it…they are engaged, informed, and stay up to date by taking advantage of benefits that ACI membership provides them.
Read more about membership
Become an ACI Member
Founded in 1904 and headquartered in Farmington Hills, Michigan, USA, the American Concrete Institute is a leading authority and resource worldwide for the development, dissemination, and adoption of its consensus-based standards, technical resources, educational programs, and proven expertise for individuals and organizations involved in concrete design, construction, and materials, who share a commitment to pursuing the best use of concrete.
ACI World Headquarters
38800 Country Club Dr.
Farmington Hills, MI
ACI Middle East Regional Office
Second Floor, Office # 02.01/07
The Offices 02 Building, One Central
Dubai World Trade Center Complex
Phone: +971.4.516.3208 & 3209
Feedback via Email
Home > Publications > International Concrete Abstracts Portal
The International Concrete Abstracts Portal is an ACI led collaboration with leading technical organizations from within the international concrete industry and offers the most comprehensive collection of published concrete abstracts.
Title: Microstructure and Mechanical Properties of Polymer- Phosphazene Mortar Exposed to Sulfate Attack
Author(s): Harun Tanyildizi
Publication: Materials Journal
Appears on pages(s): 201-208
Keywords: external sulfate attack; mechanical properties; microstructure; polymer-phosphazene mortars
Abstract:This study investigated polymer-phosphazene mortars subjected to external sulfate attack for 1 year to examine their resistance to the sulfate effect. Then, the mechanical properties and microstructure of polymer-phosphazene mortars were studied. The number of experiments was reduced by selecting the L25 orthogonal array. Samples were produced in sizes of 50 x 50 x 50 mm (1.97 x 1.97 x 1.97 in.) and 25 x 25 x 285 mm (0.98 x 0.98 x 11.22 in.). The samples were dried at 105 ± 5°C (221 ± 9°F) for 24 hours after curing for 28 days. Later, the monomer containing phosphazene was impregnated to samples at atmospheric conditions for 1 day. The polymerizations of samples were carried out at 60°C (140°F) for 4 hours. These samples were subjected to sulfate attack for 30, 60, 90, 180, and 365 days. The compressive strength, weight, and length changes of polymerphosphazene mortars subjected to external sulfate attack were determined. After the external sulfate attack, scanning electron microscope (SEM), energy-dispersive X-ray (EDX), and X-ray diffraction (XRD) analyzes of the samples were carried out. The analysis of variance (ANOVA) results showed that the most effective parameter was cement dosage. The results showed that sulfate was prevented from entering into the concrete as cracks and voids in the samples were filled with phosphazene polymers.