Title: Properties of Flowable Slurry Containing Wood Ash

Author(s): T. R. Naik, R. N. Kraus, Y. Chun, and R. Siddique

Publication: Symposium Paper

Volume: 219


Appears on pages(s): 85-98

Keywords: bleed water; cement; compressive strength; controlled low-strength materials (CLSM); flowable slurry; permeability; wood ash

DOI: 10.14359/13141

Date: 3/1/2004

Three series of flowable slurry mixtures were made, each series with three different sources of wood ash (W-1, W-2, and W-3). The series of mixtures were: low-strength (0.3 to 0.7 MPa), medium-strength (0.7 to 3.5 MPa), and high-strength (3.5 to 8 MPa) mixtures. Tests were performed for flow, air content, unit weight, bleeding, settlement, compressive strength, and water permeability. Wood ashes W-1 and W-3 caused expansive reactions in CLSM mixtures resulting in little or slight (average 1%) net shrinkage of CLSM. Wood ash W-2 caused either significant net swelling (15% for Mixture 2-L, and 21% for Mixture 2-M) or no shrinkage (Mixture 2-H) of CLSM. The 91-day compressive strength of low-strength, medium-strength, and high-strength slurry mixtures was in the ranges of 0.38 to 0.97 MPa, 1.59 to 5.28 MPa, and 4.00 to 8.62 MPa, respectively. Overall, the slurry mixtures showed an average increase in strength of 150% (range: 25% to 450%) between the ages of 28 days and 91 days. This was attributed to pozzolanic and cementitious reactions of wood ash. In general, water permeability of CLSM mixtures decreased with age.