Fly Ash-Based Lightweight Geopolymer Mortars for Fire Protection
Author(s):
Lorenza Carabba, Gregor J. G. Gluth, Stephan M. Pirskawetz, Simone Krüger, and Maria Chiara Bignozzi
Publication:
Symposium Paper
Volume:
326
Issue:
Appears on pages(s):
26.1-26.10
Keywords:
alkali activated materials, expanded perlite, fly ash, geopolymers, room temperature curing, standard fire curves, passive fire protection
DOI:
10.14359/51711008
Date:
8/10/2018
Abstract:
The present study aims to investigate the use of geopolymer mortars as passive fire protection system for steel structures. Coal fly ashes were used as aluminosilicate source and perlite was employed as aggregate to obtain a lightweight system. In addition, a geopolymer mortar containing quartz aggregate was produced for comparison. The geopolymer mortars were applied on stainless steel plates and exposed to both, cellulosic and hydrocarbon standard fire curves, according to ISO 834-1 and EN 1363-2, respectively. Acoustic emission measurements were conducted to analyze cracking phenomena during the high temperature exposure. The resulting temperature-time curves showed that the investigated system is effective in retarding the temperature rise of the steel plates. When the cellulosic fire curve was applied, a 20 mm [0.79 in.] thick layer of lightweight geopolymer mortar protected the steel substrate from reaching the critical temperature of 500 °C [932 °F] for at least 30 minutes, avoiding the rapid decrease of its mechanical properties and thus representing an important safety measure against accidental fires. No spalling phenomena on heating were detected; however, significant cracking was observed on cooling.
Related References:
1. American Petroleum Institute, 1999, “Fireproofing Practices in Petroleum and Petrochemical Processing Plants”, API Publication 2218.
2. Porcari, G.F., Zalok, E., Mekky, W., 2015, “Fire induced progressive collapse of steel building structures: A review of the mechanisms”, Engineering Structures, 82, 261–267.
3. Provis, J.L., 2017, “Alkali-activated materials”, Cement and Concrete Research - in press, doi: 10.1016/j.cemconres.2017.02.009
4. Jamieson, E., McLellan, B., van Riessen, A., Nikraz, H., 2015, “Comparison of embodied energies of Ordinary Portland Cement with Bayer-derived geopolymer products”, Journal of Cleaner Production, 99, 112–118.
5. Ouellet-Plamondon, C., Habert, G., 2015, “Life cycle assessment (LCA) of alkali-activated cements and concretes”, Handbook of Alkali-Activated Cements, Mortars and Concretes, Woodhead Publishing, Oxford, 663–686.
6. Krivenko, P., 2017, “Why alkaline activation – 60 years of the theory and practice of alkali-activated materials”, Journal of Ceramic Science and Technology, 8, 323–334.
7. Panias, D., Balomenos, E., Sakkas, K., 2015, “The fire resistance of alkali-activated cement-based concrete binders”, Handbook of Alkali-Activated Cements, Mortars and Concretes, Woodhead Publishing, Oxford, 423–461.
8. Rickard, W.D.A., Gluth, G.J.G., Pistol, K., 2016, “In-situ thermo-mechanical testing of fly ash geopolymer concretes made with quartz and expanded clay aggregates”, Cement and Concrete Research, 80, 33–43.
9. Rickard, W.D.A., Temuujin, J., van Riessen, A., 2012, “Thermal analysis of geopolymer pastes synthesised from five fly ashes of variable composition”, Journal of Non-Crystalline Solids, 58, 1830–1839.
10. Temuujin, J., Minjigmaa, A., Rickard, W., Lee, M., Williams, I., van Riessen, A., 2010, “Fly ash based geopolymer thin coatings on metal substrates and its thermal evaluation”, Journal of Hazardous Materials, 180, 748–752.
11. Watolla, M.-B., Gluth, G.J.G., Sturm, P., Rickard, W.D.A., Krüger, S., Schartel, B., 2017, “Intumescent Geopolymer-Bound Coatings for Fire Protection of Steel”, Journal of Ceramic Science and Technology, 8, 351–364.
12. Rickard, W.D.A., van Riessen, A., 2014, “Performance of solid and cellular structured fly ash geopolymers exposed to a simulated fire”, Cement and Concrete Composites, 48, 75–82.
13. Rickard, W.D.A., Vickers, L., van Riessen, A., 2013, “Performance of fibre reinforced, low density metakaolin geopolymers under simulated fire conditions”, Applied Clay Science, 73, 71–77.
14. Sakkas, K., Panias, D., Nomikos, P.P., Sofianos, A.I., 2014, “Potassium based geopolymer for passive fire protection of concrete tunnels linings”, Tunnelling and Underground Space Technology, 43, 148–156.
15. Carabba, L., Santandrea, M., Carloni, C., Manzi, S., Bignozzi, M.C., 2017, “Steel fiber reinforced geopolymer matrix (S-FRGM) composites applied to reinforced concrete structures for strengthening applications: A preliminary study”, Composites Part B: Engineering, 128, 83–90.
16. Krüger, S., Gluth, G.J.G., Watolla, M.-B., Morys, M., Häßler, D., Schartel, B., 2016, “New ways: reactive fire protection coatings for extreme conditions (in German)”, Bautechnik, 93, 531–542.
17. White, C.E., Provis, J.L., Proffen, T., Van Deventer, J.S.J., 2010, “the effects of temperature on the local structure of metakaolin-based geopolymer binder: a neutron pair distribution function investigation”, Journal of the American Ceramic Society, 93, 3486–3492.
18. Duxson, P., Lukey, G.C., van Deventer, J.S.J., 2006, “Thermal conductivity of metakaolin geopolymers used as a first approximation for determining gel interconnectivity”, Industrial & Engineering Chemistry Research, 45, 7781–7788.
19. Novais, R.M., Buruberri, L.H., Ascensão, G., Seabra, M.P., Labrincha, J.A., 2016, “Porous biomass fly ash-based geopolymers with tailored thermal conductivity”, Journal of Cleaner Production, 119, 99–107.
20. Masi, G., Rickard, W.D.A., Bignozzi, M.C., van Riessen, A., 2015, “The effect of organic and inorganic fibres on the mechanical and thermal properties of aluminate activated geopolymers”, Composites Part B: Engineering, 76, 218–228.
21. Gluth, G.J.G., Rickard, W.D.A., Werner, S., Pirskawetz, S., 2016, “Acoustic emission and microstructural changes in fly ash geopolymer concretes axposed to simulated fire”, Materials and Structures, 49, 5243–5254
22. Carabba, L., Manzi, S., Rambaldi, E., Ridolfi, G., Bignozzi, M.C., 2017, “High-temperature behaviour of alkali-activated composited based on fly ash and recycled refractory particles”, Journal of Ceramic Science and Technology, 8, 377-388.
23. Bakharev, T., 2006, “Thermal behavior of geopolymers prepared using class F fly ash and elevated temperature curing”, Cement and Concrete research, 36, 1134–1147.
24. Zhao R, Sanjayan JG., 2011, “Geopolymer and Portland cement concretes in simulated fire”, Magazine of Concrete Research, 63, 163–173.
25. Duxson, P., Lukey, G.C., van Deventer, J.S.J., 2007, “The thermal evolution of metakaolin geopolymers: Part 2 – Phase stability and structural development”, Journal of Non-Crystalline Solids, 353, 2186–2200.
26. Kong, D.L.Y., Sanjayan, J.G., Sagoe-Crentsil, K., 2008, “Factors affecting the performance of metakaolin geopolymers exposed to elevated temperatures”, Journal of Materials Science, 43, 824–831.
27. Sotiriadis, K., Guzii, S., Kumpová, I., Mácová, P., Viani, A., 2017, “The effect of firing temperature on the composition and microstructure of a geocement-based binder of sodium water-glass”, Solid State Phenomena, 267, 58–62.