Title:
CO2-Sequestered Cast-in-Place Engineered Cementitious Composites
Author(s):
Duo Zhang and Victor C. Li
Publication:
Materials Journal
Volume:
120
Issue:
1
Appears on pages(s):
29-40
Keywords:
carbon mineralization; carbonation; CO2 sequestration; durability; engineered cementitious composite (ECC); fly ash; life-cycle assessment; steel slag; sustainability
DOI:
10.14359/51737331
Date:
1/1/2023
Abstract:
The built environment is facing an increasing challenge of reducing emissions regarding both embodied and operational carbon. As an ultra-durable concrete, engineered cementitious composites (ECC) reduce the need for repair, thus resulting in a prominent reduction of life-cycle footprints. Herein, a new version of low-carbon ECC was developed for cast-in-place applications by sequestering CO2 through mineralization. Two waste streams were pre-carbonated and incorporated into ECC as fine aggregate and supplementary cementitious material, respectively. At 28 days, the CO2-sequestered ECC exhibited a compressive strength of 32.2 MPa (4670 psi), tensile strength of 3.5 MPa (508 psi), and strain capacity of 2.9%. Multiple fine cracks were distinctly identified, with a residual crack width of 38 μm (0.0015 in.) and a selfhealing behavior comparable to that of conventional ECC. The new ECC sequestered 97.7 kg/m3 (164.7 lb/yd3) CO2 (equivalent to 4.7 wt% of final mixture) and demonstrated a 42% reduction in cradle-to-gate emissions compared to conventional concrete at the same strength level. This study demonstrates the viability of turning waste CO2 gas into durable construction materials and proposes a potential path towards carbon neutrality.
Related References:
1. Barcelo, L.; Kline, J.; Walenta, G.; and Gartner, E., “Cement and Carbon Emissions,” Materials and Structures, V. 47, No. 6, 2014, pp. 1055-1065. doi: 10.1617/s11527-013-0114-5
2. Zhang, D.; Ghouleh, Z.; Shao, Y., “Review on Carbonation Curing of Cement-Based Materials,” Journal of CO2 Utilization, V. 21, 2017, pp. 119-131.
3. Berger, R.; Young, J.; and Leung, K., “Acceleration of Hydration of Calcium Silicates by Carbon Dioxide Treatment,” Nature. Physical Science (London), V. 240, No. 97, 1972, pp. 16-18. doi: 10.1038/physci240016a0
4. Vandeperre, L., and Al-Tabbaa, A., “Accelerated Carbonation of Reactive MgO Cements,” Advances in Cement Research, V. 19, No. 2, 2007, pp. 67-79. doi: 10.1680/adcr.2007.19.2.67
5. Cizer, Ö.; Van Balen, K.; Elsen, J.; and Van Gemert, D., “Real-Time Investigation of Reaction Rate and Mineral Phase Modifications of Lime Carbonation,” Construction and Building Materials, V. 35, 2012, pp. 741-751. doi: 10.1016/j.conbuildmat.2012.04.036
6. Monkman, S., and MacDonald, M., “On Carbon Dioxide Utilization as a Means to Improve the Sustainability of Ready-Mixed Concrete,” Journal of Cleaner Production, V. 167, 2017, pp. 365-375. doi: 10.1016/j.jclepro.2017.08.194
7. Li, V. C., “On Engineered Cementitious Composites (ECC). A Review of the Material and Its Applications,” Journal of Advanced Concrete Technology, V. 1, No. 1, 2003, pp. 215-230. doi: 10.3151/jact.1.215
8. Li, V. C., Engineered Cementitious Composites (ECC): Bendable Concrete for Sustainable and Resilient Infrastructure, Springer, New York, 2019.
9. Li, V. C., “Engineered Cementitious Composites (ECC)—Tailored Composites through Micromechanical Modeling,” Fiber Reinforced Concrete Present and Future, N. Banthia, A. Bentur, and A. A. Mufti, eds., Canadian Society for Civil Engineering, Montreal, QC, Canada, 1997, pp. 64-97.
10. Yang, E. H., and Li, V. C., “A Micromechanical Model for Fiber Cement Optimization and Component Tailoring,” 10th International Inorganic-Bonded Fiber Composites Conference, Sao Paulo, Brazil, 2006.
11. Li, M., and Li, V. C., “Cracking and Healing of Engineered Cementitious Composites under Chloride Environment,” ACI Materials Journal, V. 108, No. 3, May-June 2011, pp. 333-340.
12. Lepech, M. D., and Li, V. C., “Water Permeability of Engineered Cementitious Composites,” Cement and Concrete Composites, V. 31, No. 10, 2009, pp. 744-753. doi: 10.1016/j.cemconcomp.2009.07.002
13. Li, V. C., and Yang, E. H., “Self Healing in Concrete Materials,” Self-Healing Materials, Springer, Dordrecht, the Netherlands, 2007, pp. 161-193.
14. Li, V. C., and Herbert, E., “Robust Self-Healing Concrete for Sustainable Infrastructure,” Journal of Advanced Concrete Technology, V. 10, No. 6, 2012, pp. 207-218. doi: 10.3151/jact.10.207
15. Keoleian, G. A.; Kendall, A.; Dettling, J. E.; Smith, V. M.; Chandler, R. F.; Lepech, M. D.; and Li, V. C., “Life Cycle Modeling of Concrete Bridge Design: Comparison of Engineered Cementitious Composite Link Slabs and Conventional Steel Expansion Joints,” Journal of Infrastructure Systems, ASCE, V. 11, No. 1, 2005, pp. 51-60. doi: 10.1061/(ASCE)1076-0342(2005)11:1(51)
16. Zhang, D.; Ellis, B. R.; Jaworska, B.; Hu, W.-H.; and Li, V. C., “Carbonation Curing for Precast Engineered Cementitious Composites,” Construction and Building Materials, V. 313, 2021, p. 125502. doi: 10.1016/j.conbuildmat.2021.125502
17. Wu, H.-L.; Zhang, D.; Ellis, B. R.; and Li, V. C., “Development of Reactive MgO-Based Engineered Cementitious Composite (ECC) through Accelerated Carbonation Curing,” Construction and Building Materials, V. 191, 2018, pp. 23-31. doi: 10.1016/j.conbuildmat.2018.09.196
18. Scrivener, K.; Martirena, F.; Bishnoi, S.; and Maity, S., “Calcined Clay Limestone Cements (LC3),” Cement and Concrete Research, V. 114, 2018, pp. 49-56. doi: 10.1016/j.cemconres.2017.08.017
19. JSCE, Recommendations for Design and Construction of High Performance Fiber Reinforced Cement Composites with Multiple Fine Cracks (HPFRCC), Tokyo, Japan, 2008.
20. Baciocchi, R.; Costa, G.; Polettini, A.; and Pomi, R., “Influence of Particle Size on the Carbonation of Stainless Steel Slag for CO2 Storage,” Energy Procedia, V. 1, No. 1, 2009, pp. 4859-4866. doi: 10.1016/j.egypro.2009.02.314
21. Huijgen, W. J.; Witkamp, G.-J.; and Comans, R. N., “Mineral CO2 Sequestration by Steel Slag Carbonation,” Environmental Science & Technology, V. 39, No. 24, 2005, pp. 9676-9682. doi: 10.1021/es050795f
22. Kan, L.; Shi, R.; and Zhu, J., “Effect of Fineness and Calcium Content of Fly Ash on the Mechanical Properties of Engineered Cementitious Composites (ECC),” Construction and Building Materials, V. 209, 2019, pp. 476-484. doi: 10.1016/j.conbuildmat.2019.03.129
23. Mehta, P. K., “Influence of Fly Ash Characteristics on the Strength of Portland-Fly Ash Mixtures,” Cement and Concrete Research, V. 15, No. 4, 1985, pp. 669-674. doi: 10.1016/0008-8846(85)90067-5
24. Nguyen, L.; Moseson, A. J.; Farnam, Y.; and Spatari, S., “Effects of Composition and Transportation Logistics on Environmental, Energy and Cost Metrics for the Production of Alternative Cementitious Binders,” Journal of Cleaner Production, V. 185, 2018, pp. 628-645. doi: 10.1016/j.jclepro.2018.02.247
25. PCA, “Environmental Product Declaration—Portland Cement,” Portland Cement Association, Skokie, IL, 2021.
26. EFCA, “Environmental Product Declaration—Concrete Admixtures – Plasticisers and Superplasticisers,” European Federation of Concrete Admixtures Associations Ltd., 2015.
27. Miller, S. A.; John, V. M.; Pacca, S. A.; and Horvath, A., “Carbon Dioxide Reduction Potential in the Global Cement Industry by 2050,” Cement and Concrete Research, V. 114, 2018, pp. 115-124. doi: 10.1016/j.cemconres.2017.08.026
28. Bushi, L., and Finlayson, G., “NRMCA Member National and Regional Life Cycle Assessment Benchmark (Industry Average) Report,” National Ready Mixed Concrete Association, Alexandria, VA, Oct. 2014.