Title:
Role of Alkalis in Natural Pozzolans on Alkali-Silica Reaction
Author(s):
R. D. Kalina, S. Al-Shmaisani, S. Seraj, R. Cano, R. D. Ferron, and M. C. G. Juenger
Publication:
Materials Journal
Volume:
118
Issue:
3
Appears on pages(s):
83-89
Keywords:
accelerated testing; alkali content; alkali-silica reaction; fly ash; natural pozzolans; supplementary cementitious materials
DOI:
10.14359/51732598
Date:
5/1/2021
Abstract:
Fly ashes with high alkali contents have been observed to be less effective in controlling expansion due to alkali-silica reaction (ASR) in concrete than low-alkali fly ashes, a problem that can be hard to predict using accelerated testing. Many natural pozzolans have high alkali contents, and there is concern that these alkalis may likewise reduce their effectiveness in ASR control and affect accelerated test results. This study examines the performance of natural pozzolans in ASR testing. The mineralogies of the natural pozzolans were determined using Rietveld quantitative X-ray diffraction (XRD), and the compositions of the natural pozzolans were determined using X-ray fluorescence spectroscopy (XRF) and available alkali testing. The results suggest that the available alkalis from fly ashes and natural pozzolans are different, and high-alkali natural pozzolans perform well in both the accelerated mortar bar and concrete prism tests for ASR.
Related References:
1. Juenger, M. C. G.; Snellings, R.; and Bernal, S. A., “Supplementary Cementitious Materials: New Sources, Characterization, and Performance Insights,” Cement and Concrete Research, V. 122, Aug. 2019, pp. 257-273. doi: 10.1016/j.cemconres.2019.05.008
2. Stanton, T. E., “Studies of Use of Pozzolans for Counteracting Excessive Concrete Expansion Resulting from Reaction between Aggregates and the Alkalies in Cement,” Symposium on Use of Pozzolanic Materials in Mortars and Concretes, ASTM STP99, T. Stanton, and R. Blanks, ed., American Society of Civil Engineers, ASTM International, West Conshohocken, PA, August 1950, pp. 178-203.
3. Thomas, M., “The Effect of Supplementary Cementing Materials on Alkali–Silica Reaction: A Review,” Cement and Concrete Research, V. 41, No. 12, 2011, pp. 1224-1231. doi: 10.1016/j.cemconres.2010.11.003
4. Lindgård, J.; Andiç-Çakır, Ö.; Fernandes, I.; Rønning, T. F.; and Thomas, M. D. A., “Alkali-Silica Reactions (ASR): Literature Review on Parameters Influencing Laboratory Performance Testing,” Cement and Concrete Research, V. 42, No. 2, 2012, pp. 223-243. doi: 10.1016/j.cemconres.2011.10.004
5. Rajabipour, F.; Giannini, E.; Dunant, C.; Ideker, J. H.; and Thomas, M. D. A., “Alkali-Silica Reaction: Current Understanding of the Reaction Mechanisms and the Knowledge Gaps,” Cement and Concrete Research, V. 76, Oct, 2015, pp. 130-146. doi: 10.1016/j.cemconres.2015.05.024
6. Kalina, R. D.; Al-Shmaisani, S.; Ferron, R. D.; and Juenger, M. C. G., “False Positives in ASTM C618 Specifications for Natural Pozzolans,” ACI Materials Journal, V. 116, No. 1, Jan. 2019, pp. 165-172. doi: 10.14359/51712243
7. Thomas, M.; Fournier, B.; Folliard, K.; Ideker, J.; and Shehata, M., “Test Methods for Evaluating Preventive Measures for Controlling Expansion due to Alkali-Silica Reaction in Concrete,” Cement and Concrete Research, V. 36, No. 10, 2006, pp. 1842-1856. doi: 10.1016/j.cemconres.2006.01.014
8. Shehata, M. H.; Thomas, M. D. A.; and Bleszynski, R. F., “The Effects of Fly Ash Composition on the Chemistry of Pore Solution in Hydrated Cement Pastes,” Cement and Concrete Research, V. 29, No. 12, 1999, pp. 1915-1920. doi: 10.1016/S0008-8846(99)00190-8
9. Ahmadi, B., and Shekarchi, M., “Use of Natural Zeolite as a Supplementary Cementitious Material,” Cement and Concrete Composites, V. 32, No. 2, 2010, pp. 134-141. doi: 10.1016/j.cemconcomp.2009.10.006
10. Ramasamy, U., and Tikalsky, P., “Evaluation Report of Hess Pumice,” Report for Hess Pumice Products, The University of Utah, Salt Lake City, UT, 2012.
11. Gökce, H. S.; Simsek, O.; and Korkmaz, S., “Reduction of Alkali–Silica Reaction Expansion of Mortars by Utilisation of Pozzolans,” Magazine of Concrete Research, V. 65, No. 7, 2013, pp. 441-447. doi: 10.1680/macr.12.00118
12. Bektas, F.; Turanli, L.; and Monteiro, P. J. M., “Use of Perlite Powder to Suppress the Alkali–Silica Reaction,” Cement and Concrete Research, V. 35, No. 10, 2005, pp. 2014-2017. doi: 10.1016/j.cemconres.2004.10.029
13. Hossain, K. M. A., “Volcanic Ash and Pumice as Cement Additives: Pozzolanic, Alkali–Silica Reaction and Autoclave Expansion Characteristics,” Cement and Concrete Research, V. 35, No. 6, 2005, pp. 1141-1144. doi: 10.1016/j.cemconres.2004.09.025
14. Mahyar, M.; Erdoğan, S. T.; and Tokyay, M., “Extension of the Chemical Index Model for Estimating Alkali–Silica Reaction Mitigation Efficiency to Slags and Natural Pozzolans,” Construction and Building Materials, V. 179, No. 10, 2018, pp. 587-597. doi: 10.1016/j.conbuildmat.2018.05.217
15. Diaz-Loya, I.; Juenger, M.; Seraj, S.; and Minkara, R., “Extending Supplementary Cementitious Material Resources: Reclaimed and Remediated Fly Ash and Natural Pozzolans,” Cement and Concrete Composites, V. 101, Aug, 2019, pp. 44-51. doi: 10.1016/j.cemconcomp.2017.06.011
16. Seraj, S.; Cano, R.; Ferron, R. D.; and Juenger, M. C. G., “The Role of Particle Size on the Performance of Pumice as a Supplementary Cementitious Material,” Cement and Concrete Composites, V. 80, July, 2017, pp. 135-142. doi: 10.1016/j.cemconcomp.2017.03.009
17. Seraj, S.; Cano, R.; Liu, S.; Whitney, D.; Fowler, D.; Ferron, R.; Zhu, J.; and Juenger, M., “Evaluating the Performance of Alternative Supplementary Cementing Material in Concrete,” FHWA/TX-14/0-6717-1, Center for Transportation Research at the University of Texas at Austin, Austin, TX, Oct. 2014.
18. Thomas, M. D. A., and Innis, F. A., “Use of the Accelerated Mortar Bar Test for Evaluating the Efficacy of Mineral Admixtures for Controlling Expansion due to Alkali–Silica Reaction,” Cement, Concrete and Aggregates, V. 21, No. 2, 1999, pp. 157-164. doi: 10.1520/CCA10429J
19. Neal, R. E.; Thomas, M. D. A.; and Shashiprakash, S., “Innocuous Behavior of Alkalies Derived from Pulverized Calcined Shale: A Natural Pozzolan,” Proceedings, Eleventh International Conference on Alkali-Aggregate Reaction in Concrete, Quebec City, QC, Canada, 2000, pp. 713-721.
20. Duchesne, J., and Berube, M., “Available Alkalies from Supplementary Cementing Materials,” ACI Materials Journal, V. 91, No. 3, May-June 1994, pp. 289-299.
21. Shehata, M. H., and Thomas, M. D. A., “Alkali Release Characteristics of Blended Cements,” Cement and Concrete Research, V. 36, No. 6, 2006, pp. 1166-1175. doi: 10.1016/j.cemconres.2006.02.015
22. Shehata, M. H., and Thomas, M. D. A., “The Role of Alkali Content of Portland Cement on the Expansion of Concrete Prisms Containing Reactive Aggregates and Supplementary Cementing Materials,” Cement and Concrete Research, V. 40, No. 4, 2010, pp. 569-574. doi: 10.1016/j.cemconres.2009.08.009
23. Shehata, M. H., and Thomas, M. D. A., “The Effect of Fly Ash Composition on the Expansion of Concrete due to Alkali-Silica Reaction,” Cement and Concrete Research, V. 30, No. 7, 2000, pp. 1063-1072. doi: 10.1016/S0008-8846(00)00283-0
24. Mehta, P. K., “Natural Pozzolans,” Supplementary Cementing Materials for Concrete, SP86-8E, V. M. Malhotra, ed., Minister of Supply and Services Canada, CANMET, Ottawa, ON, Canada, 1987, pp. 3-33.
25. Pepper, L., and Mather, B., “Effectiveness of Mineral Admixtures in Preventing Excessive Expansion of Concrete due to Alkali-Aggregate Reaction,” Proceedings, American Society for Testing Materials, V. 59, ASTM International, West Conshohocken, PA, 1959, pp. 1178-1203.
26. Roy, D. M.; Luke, K.; and Diamond, S., “Characterization of Fly Ash and Its Reactions in Concrete,” Materials Research Society Symposium Proceedings, V. 43, Materials Research Society, Warrendale, PA, 1985, pp. 3-20.
27. McCarthy, G. J.; Swanson, K. D.; Keller, L. P.; and Blatter, W. C., “Mineralogy of Western Fly Ash,” Cement and Concrete Research, V. 14, No. 4, 1984, pp. 471-478. doi: 10.1016/0008-8846(84)90121-2
28. Mehta, P. K., “Pozzolanic and Cementitious By-Products in Concrete—Another Look,” Proceedings, Third International Conference on Fly Ash, Silica Fume, Slag, and Natural Pozzolans in Concrete, SP-114, V. M. Malhotra, ed., American Concrete Institute, Farmington Hills, MI, 1989, pp. 1-43.
29. Thomas, M. D. A.; Shehata, M. H.; and Shashiprakash, S. G., “The Use of Fly Ash in Concrete: Classification by Composition,” Cement, Concrete and Aggregates, V. 21, No. 2, 1999, pp. 105-110. doi: 10.1520/CCA10423J
30. Aughenbaugh, K. L.; Chancey, R. T.; Stutzman, P.; Juenger, M. C. G.; and Fowler, D. W., “An Examination of the Reactivity of Fly Ash in Cementitious Pore Solutions,” Materials and Structures, V. 46, No. 5, 2013, pp. 869-880. doi: 10.1617/s11527-012-9939-6
31. Hemmings, R. T., and Berry, E. E., “On the Glass in Coal Fly Ashes: Recent Advances,” Materials Research Society Symposium Proceedings, V. 113, Materials Research Society, Warrendale, PA, 1988, pp. 3-38.
32. ASTM C311-18, “Standard Test Method for Sampling and Testing Fly Ash or Natural Pozzolans for Use in Portland-Cement Concrete,” ASTM International, West Conshohocken, PA, 2018.
33. Rodríguez-Camacho, R. E., and Uribe-Afif, R., “Importance of Using the Natural Pozzolans on Concrete Durability,” Cement and Concrete Research, V. 32, No. 12, 2002, pp. 1851-1858. doi: 10.1016/S0008-8846(01)00714-1
34. ASTM C1567-13, “Standard Test Method for Determining the Potential Alkali–Silica Reactivity of Combinations of Cementitious Materials and Aggregate (Accelerated Mortar-Bar Method),” ASTM International, West Conshohocken, PA, 2013.
35. ASTM C1293-20, “Standard Test Method for Determination of Length Change of Concrete due to Alkali-Silica Reaction,” ASTM International, West Conshohocken, PA, 2020.
36. ASTM C1260-14, “Standard Test Method for Potential Alkali Reactivity of Aggregates (Mortar-Bar Method),” ASTM International, West Conshohocken, PA, 2014.
37. Bérubé, M.; Duchesne, J.; and Chouinard, D., “Why the Accelerated Mortar Bar Method ASTM C 1260 Is Reliable for Evaluating the Effectiveness of Supplementary Cementing Materials in Suppressing Expansion due to Alkali–Silica Reactivity,” Cement, Concrete and Aggregates, V. 17, No. 1, 1995, pp. 26-34. doi: 10.1520/CCA10333J
38. Thomas, M. D. A.; Fournier, B.; Folliard, K. J.; Shehata, M. H.; Ideker, J. H.; and Rogers, C., “Performance Limits for Evaluating Supplementary Cementing Materials Using Accelerated Mortar Bar Test,” ACI Materials Journal, V. 104, No. 2, Mar.-Apr. 2007, pp. 115-122.
39. Rogers, C. A., and Hooton, R. D., “Reduction in Mortar and Concrete Expansion with Reactive Aggregates due to Alkali Leaching,” Cement, Concrete and Aggregates, V. 13, No. 1, 1991, pp. 42-49. doi: 10.1520/CCA10548J
40. Rivard, P.; Berube, M. A.; Ollivier, J. P.; and Ballivy, G., “Decrease of Pore Solution Alkalinity in Concrete Tested for Alkali–Silica Reaction,” Materials and Structures, V. 40, No. 9, 2007, pp. 909-921. doi: 10.1617/s11527-006-9191-z
41. ASTM C1778-19, “Standard Guide for Reducing the Risk of Deleterious Alkali Aggregate Reaction in Concrete,” ASTM International, West Conshohocken, PA, 2019.
42. ASTM C150/C150M-19, “Standard Specification for Portland Cement,” ASTM International, West Conshohocken, PA, 2019.
43. ASTM C604-18, “Standard Test Method for True Specific Gravity of Refractory Materials by Gas-Comparison Pycnometer,” ASTM International, West Conshohocken, PA, 2018.
44. Deer, W. A.; Howie, R. A.; and Zussman, J., An Introduction to the Rock-Forming Minerals, third edition, Mineralogical Society, London, UK, 2013.