Calcium oxychloride formation in pastes containing supplementary cementitious materials: Thoughts on the role of cement and supplementary cementitious materials reactivity

ABOUT THE INTERNATIONAL CONCRETE ABSTRACTS PORTAL

  • The International Concrete Abstracts Portal is an ACI led collaboration with leading technical organizations from within the international concrete industry and offers the most comprehensive collection of published concrete abstracts.

International Concrete Abstracts Portal

  


Title: Calcium oxychloride formation in pastes containing supplementary cementitious materials: Thoughts on the role of cement and supplementary cementitious materials reactivity

Author(s): Prannoy Suraneni; Vahid Jafari Azad; Burkan O. Isgor; William Jason Weiss

Publication: RILEM

Volume: 1

Issue:

Appears on pages(s): 24-30

Keywords: deicing salts; calcium oxychloride; differential scanning calorimetry; thermogravimetric analysis, thermodynamic analysis

Date: 5/29/2016

Abstract:
Over the last decade many concrete pavements in North America have begun to show excessive damage at the joints. This damage appears to be due to two primary causes: classic freeze-thaw damage due to local saturation caused by the pooling of water at the joints, and formation of an expansive phase known as calcium oxychloride due to a reaction between chloride-based deicing salts and calcium hydroxide in concrete. This letter explores the formation of calcium oxychloride in cementitious matrices based on constituent materials and mixture compositions. Low temperature differential scanning calorimetry and thermogravimetric analysis were used to quantify the amount of calcium oxychloride and calcium hydroxide, respectively. Thermodynamic modeling was used to predict calcium hydroxide contents from the constituent material compositions. It is shown that calcium oxychloride contents are well correlated with calcium hydroxide contents in cementitious pastes. Supplementary cementitious materials, such as fly ash and slag, can reduce calcium oxychloride formation by reducing the amount of calcium hydroxide. Complexities in the determination of reactivity of supplementary cementitious materials based on their replacement level and different water-to-cement ratios are discussed. Although it is clear that supplementary cementitious materials are beneficial in reducing calcium oxychloride formation, additional analysis tools are needed to more accurately quantify the specific mechanisms (such as dilution, pozzolanic or hydraulic reaction, changes in cement hydration) that result in the beneficial aspects of each supplementary cementitious material.