Title:
Multi-Scale Fiber Reinforcement for Cracking Resistance in Cement Mortars
Author(s):
Joshua Hogancamp, Cesario Tavares, and Zachary Grasley
Publication:
Symposium Paper
Volume:
335
Issue:
Appears on pages(s):
1-11
Keywords:
Carbon nanofiber; carbon microfiber; mortar; cracking resistance
DOI:
10.14359/51720211
Date:
9/20/2019
Abstract:
The current state of the art in fiber-reinforced cement-based materials indicates that adding multiple fiber types or sizes primarily creates a superpositioned behavior state: the behavior from each fiber type separately is added to the composite behavior of the material. Carbon nanofibers (CNFs) and milled carbon microfibers (MCMFs) can increase cracking resistance in cement-based materials by bridging cracks, although CNFs bridge cracks significantly smaller than cracks bridged by MCMFs. This research suggests that multi-scale fiber reinforcement
(CNFs with MCMFs) might add compounded benefits to cracking resistance. Tests evaluating cracking resistance were performed utilizing a restrained-ring drying shrinkage test with Portland cement mortars. The CNFs and/or MCMFs were pre-mixed with cement using a sonication/distillation technique and/or rotary tumbling. Concentrations of CNFs and MCMFs were tested up to 5% and 6% by mass of cement, respectively. Restrained ring tests on mortar with high concentrations of CNFs or MCMFs reveal delayed cracking time by factors up to 6.4 or 2.6, respectively. Combining CNFs with MCMFs delayed cracking by a factor of at least 52. The increase in cracking resistance is attributed to the combined effects of bridging cracks of multiple sizes.
Related References:
1. Mindess S, Young FJ, Darwin D. Concrete, 2nd Edition: Pearson Education, Inc.; 2003.
2. Cao J, Chung DDL. Improving the dispersion of steel fibers in cement mortar by the addition of silane.Cement and Concrete Research. 2001;31:309-11.
3. Zheng Z, Feldman D. Synthetic Fibre-Reinforced Concrete. Progress in Polymer Science. 1995;20(2):185-210.
4. Mahadik SA, Kamane SK, Lande AC. Effect of steel fibers on compressive and flexural strength of concrete. International Journal of Advanced Structures and Geotechnical Engineering. 2014;3(4):388-92.
5. Lok TS, Xiao JR. Flexural strength assessment of steel fiber reinforced concrete. Journal of Materials in Civil Engineering. 1999;11(3):188-96.
6. Bentur A, Mindess S. Fiber Reinforced Cementitious Composites: Elsevier Science Publishers LTD; 1990.
7. Balaguru PN, Shah SP. Fiber-Reinforced Cement Composites: McGraw-Hill; 1992.
8. Zollo RF. Fiber-reinforced Concrete: an Overview after 30 Years of Development. Cement and Concrete Composites. 1997;19(2):107-22.
9. Yazdanbakhsh A, Grasley Z, Tyson B, Abu Al-Rub RK. Dispersion quantification of inclusions in composites. Composites Part A: Applied Science and Manufacturing. 2011;42(1):75-83.
10. Chaipanich A, Nochaiya T, Wongkeo W, Torkittikul P. Compressive strength and microstructure of carbon nanotubes–fly ash cement composites. Materials Science and Engineering: A. 2010;527(4-5):1063-7.
11. Xie X, Mai Y, Zhou X. Dispersion and alignment of carbon nanotubes in polymer matrix: A review. Materials Science and Engineering: R: Reports. 2005;49(4):89-112.
12. Yazdanbakhsh A, Grasley Z, Tyson B, Abu Al-Rub RK. Distribution of Carbon Nanofibers and Nanotubes in Cementitious Composites. Transportation Research Record: Journal of the Transportation Research Board. 2010;2142:89-95.
13. Musso S, Tulliani J-M, Ferro G, Tagliaferro A. Influence of carbon nanotubes structure on the mechanical behavior of cement composites. Composites Science and Technology. 2009;69(11-12):1985-90.
14. Li GY, Wang PM, Zhao X. Mechanical behavior and microstructure of cement composites incorporating surface-treated multi-walled carbon nanotubes. Carbon. 2005;43(6):1239-45.
15. Abu Al-Rub RK, Tyson BM, Yazdanbakhsh A, Grasley Z. Mechanical Properties of Nanocomposite Cement Incorporating Surface-Treated and Untreated Carbon Nanotubes and Carbon Nanofibers. Journal of Materials in Civil Engineering. 2012;2(1):1-6.
16. Li Q, Liu J, Xu S. Progress in Research on Carbon Nanotubes Reinforced Cementitious Composites. Advances in Materials Science and Engineering. 2015;2015:1-16.
17. Metaxa ZS, Konsta-Gdoutos MS, Shah SP. Carbon nanofiber cementitious composites: Effect of debulking procedure on dispersion and reinforcing efficiency. Cement and Concrete Composites. 2013;36:25-32.
18. Metaxa ZS, Konsta-Gdoutos MS, Shah SP. Mechanical Properties and Nanostructure of Cement-Based Materials Reinforced with Carbon Nanofibers and Polyvinyl Alcohol (PVA) Microfibers. American Concrete Institute. 2010;270:115-24.
19. Hogancamp J, Grasley Z. Dispersion of High Concentrations of Carbon Nanofibers in Portland Cement Mortars. Journal of Nanomaterials. 2017;2017:1-11.
20. Hogancamp J, Grasley Z. The use of microfine cement to enhance the efficacy of carbon nanofibers with respect to drying shrinkage crack resistance of portland cement mortars. Cement and Concrete Composites. 2017;83:405-14.
21. Hogancamp J, Grasley Z, inventorsCrack Arresting Rapid-Bond Cement (CARBON). United States2017 18 July 2017.
22. Yazdanbakhsh A, Grasley Z. The theoretical maximum achievable dispersion of nanoinclusions in cement paste. Cement and Concrete Research. 2012;42(6):798-804.
23. Shah HR, Weiss J. Quantifying shrinkage cracking in fiber reinforced concrete using the ring test. Materials and Structures. 2006;39(9):887-99.
24. Grasley Z, D'Ambrosia M. Viscoelastic properties and drying stress extracted from concrete ring tests. Cement & Concrete Composites. 2010;33:171-8.
25. ASTM. ASTM C1581: Standard Test Method for Determining Age at Cracking and Induced Tensile Stress Characteristics of Mortar and Concrete under Restrained Shrinkage. ASTM International2009.
26. Hossain AB, Weiss J. The role of specimen geometry and boundary conditions on stress development and cracking in the restrained ring test. Cement and Concrete Research. 2006;36(1):189-99.