International Concrete Abstracts Portal

  


Title: Waste Glass for Use in Geopolymers

Author(s): Mary U. Christiansen and Lawrence L. Sutter

Publication: Symposium Paper

Volume: 294

Issue:

Appears on pages(s): 1-18

Keywords: alkali activation, fly ash, geopolymer, metakaolin, sodium hydroxide, waste glass.

DOI: 10.14359/51686320

Date: 10/4/2013

Abstract:
Waste glass is considered for use in a geopolymer binder systems based on the high Si content, amorphous framework structure, adequate hardness and widespread availability. A lack of Al within the system, however, must be taken into account, as Si/Al and Na/Al ratios have been shown to affect properties such as setting time, compressive strength and microstructure. Metakaolin and fly ash were added to a glass-based system, lowering the Si/Al and bringing Na/Al closer to unity. Mortars made using 100% glass as well as 25 and 50% of fly ash or metakaolin by mass were activated with 10M NaOH and cured at 80°C for 24 hours. Microstructural characterization of fracture surfaces and thin sections as well as compressive strength and degree of reaction data was collected. The 100% glass mixture (Si/Al – 8.39, Na/Al – 1.61) and 25% metakaolin (Si/Al – 4.96, Na/Al – 0.97) mixtures showed a dense, continuous microstructure. The 25% MK mix resulted in a 1-day f’c of above 5000 psi (35 MPa), while the 50% metakaolin mixture (Si/Al = 3.45, Na/Al – 0.69) developed little strength and had a low-density microstructure, possibly due to the high water demand. Mixtures containing fly ash resulted in reasonable compressive strengths and moderately dense microstructures.